Glass forging lubricant
Glass forging lubricant is essential in modern metal forging, a process that has evolved from labor-intensive methods to advanced techniques like press forging, drop forging, cold forging, and roll forging. Forging involves heating metals to workable temperatures and shaping them on an anvil, requiring substantial strength and skill. Traditional lubricants, such as soaps and mineral oils, fail at high forging temperatures as they burn or melt. Common lubricants in the aircraft industry include graphite, MoS2 (molybdenum disulfide), synthetics, and glass. Glass lubricants are particularly effective at high temperatures and are used in forging stainless steel, titanium, tungsten alloys, and nickel. They can be applied as a slurry or in powdered form, melting into a thick, viscous solution that helps separate metals from dies. Glass lubricants are also versatile, working well with copper, magnesium, and nickel.
Product name:
P/N number:
Appearance:
Applicable Process:
Operate temperature:
Glass powder for tube extrusion process
TLC-844-7
Blue-white particle
Large tonnage vertical extrusion
1150 ~ 1200℃
Application: Glass powder for the tube extrusion process is used in spraying applications, coating the inner and outer surfaces of billets. It serves as a lubricant between the extrusion needle and the inner wall of the extrusion cylinder, ensuring smooth material flow and reducing friction during high-temperature extrusion.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for tube extrusion process
TLC-GN18
Blue-white particle
Large tonnage vertical extrusion
1150 ~ 1200℃
Application: Glass powder for the tube extrusion process is used in spraying applications, coating the inner and outer surfaces of billets. It serves as a lubricant between the extrusion needle and the inner wall of the extrusion cylinder, ensuring smooth material flow and reducing friction during high-temperature extrusion.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for tube extrusion process
TLC-GW9
Blue-white particle
Large tonnage vertical extrusion
1150 ~ 1200℃
Application: Glass powder for the tube extrusion process is used in spraying applications, coating the inner and outer surfaces of billets. It serves as a lubricant between the extrusion needle and the inner wall of the extrusion cylinder, ensuring smooth material flow and reducing friction during high-temperature extrusion.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for tube extrusion process
TLC-360D96
Blue-white particle
Large tonnage vertical extrusion
1150 ~ 1200℃
Application: Glass powder for the tube extrusion process is formed into glass pads, placed on top of billets. These pads lubricate the die opening, facilitating smooth material flow and reducing friction during extrusion. This application ensures efficient operation and high-quality output in high-temperature metal forming processes.
Glass lubricant for titanium alloy hot extrusion process
TLC-TD7
Yellow-green particle
Large tonnage vertical extrusion
900 ~ 950℃
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Application: The glass lubricant for titanium alloy hot extrusion is used in titanium extrusion processes. It is formed into glass pads and placed on top of billets, providing lubrication to the die opening. This ensures smooth material flow, reduces friction, and enhances the quality and efficiency of the extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass lubricant for titanium alloy hot extrusion process
TLC-TD0
Blue-white particle
Large tonnage vertical extrusion
850 ~ 900℃
Application: The glass lubricant for titanium alloy hot extrusion is used in titanium extrusion processes. It is formed into glass pads and placed on top of billets, providing lubrication to the die opening. This ensures smooth material flow, reduces friction, and enhances the quality and efficiency of the extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for tube extrusion process
TLC-GW7
Fine-white powder
Horizontal extrusion
1150 ~ 1220℃
Application: Glass powder for the tube extrusion process is applied as an external coating on the billet surface, providing lubrication for the inner wall of the extrusion cylinder. This application ensures smooth material flow, reduces friction and wear on the equipment, and enhances the overall efficiency and quality of the extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for tube extrusion process
TLC-GN26
Blue-white particle
Horizontal vertical extrusion
1150 ~ 1220℃
Application: Glass powder for the tube extrusion process is applied as an internal coating on the billet's inner surface. This ensures effective lubrication of the extrusion needle, reducing friction and wear during the process. The application enhances the smooth flow of materials, improves the quality of the extruded tubes, and increases the efficiency of the extrusion operation.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for high-temperature alloy hot extrusion process
TLC-HDK-5
Blue-white particle
Horizontal extrusion
1120 ~ 1200℃
Application: Glass powder for high-temperature alloy hot extrusion is formed into glass pads and placed between the billet and the die. This application provides lubrication to the die opening, reducing friction and wear during the extrusion process. It ensures smooth material flow, enhances the quality of the extruded product, and improves overall process efficiency.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for high-temperature alloy hot extrusion process
TLC-HDK-27
Blue-white particle
Horizontal extrusion
1150 ~ 1240℃
Application: Glass powder for high-temperature alloy hot extrusion is formed into glass pads and placed between the billet and the die. These pads lubricate the die opening, reducing friction and wear during the extrusion process. This application ensures smooth material flow, improves the quality of extruded products, and enhances the overall efficiency and durability of the extrusion operation.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for high-temperature alloy hot extrusion process
TLC-HDK-35-3
Blue-white particle
Horizontal extrusion
1180 ~ 1260℃
Application: Glass powder for high-temperature alloy hot extrusion is formed into glass pads and placed between the billet and the die. This application provides lubrication to the die opening, reducing friction and wear during the extrusion process. It ensures smooth material flow, enhances the quality of the extruded product, and improves overall process efficiency.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for tube extrusion process
TLC-M1
Blue-white particle
Large tonnage vertical extrusion
1150 ~ 1180℃
Application: Glass powder for the tube extrusion process is used in stainless steel extrusion. It is formed into glass pads and placed on top of billets. These pads provide lubrication to the die opening, reducing friction and wear during the extrusion process. This application ensures smooth material flow, enhances product quality, and improves process efficiency.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for titanium alloy hot tube extrusion process
TLC-360W2
Blue-white particle
Horizontal extrusion
950 ~ 1050℃
Application: Glass powder for titanium alloy hot tube extrusion is used in the extrusion of titanium materials. It is applied as an internal coating on the inner surface of the billet, providing lubrication to the extrusion needle. This reduces friction and wear during the process, ensuring smooth material flow and enhancing the efficiency and quality of the extruded products.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for titanium alloy hot tube extrusion process
TLC-360W2
Blue-white particle
Horizontal extrusion
950 ~ 1050℃
Application: Glass powder for titanium alloy hot tube extrusion is used in the extrusion of titanium materials. It is applied as an internal coating on the inner surface of the billet, providing lubrication to the extrusion needle. This reduces friction and wear during the process, ensuring smooth material flow and enhancing the efficiency and quality of the extruded products.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for titanium alloy hot tube extrusion process
TLC-8-22
Fine-white powder
Horizontal extrusion
800 ~ 950℃
Application: Glass powder for titanium alloy hot tube extrusion is used in the extrusion of titanium materials. Applied as an external coating on the billet's outer surface, it provides effective lubrication for the inner wall of the extrusion cylinder. This reduces friction and wear, ensures smooth material flow, and enhances the quality and efficiency of the extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for titanium alloy hot tube extrusion process
TLC-GD-9-8
Blue-white particle
Horizontal extrusion
900 ~ 980℃
Application: Glass powder for titanium alloy hot tube extrusion is used in the extrusion of titanium materials. It is applied as an internal coating on the inner surface of the billet, providing lubrication to the extrusion needle. This reduces friction and wear during the process, ensuring smooth material flow and enhancing the efficiency and quality of the extruded products.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for titanium alloy hot tube extrusion process
TLC-GD-9-12
Blue-white particle
Horizontal extrusion
1000 ~ 1080℃
Application: Glass powder for titanium alloy hot tube extrusion is specifically used in titanium extrusion processes. It is formed into glass pads and placed between the billet and the die, providing critical lubrication to the die opening. This application reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the titanium extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass lubricants for hot extrusion processes
TLC-TD1150-1-55
Blue-white particle
Horizontal extrusion
1000 ~ 1080℃
Application: Glass lubricant for the hot extrusion of titanium alloy profiles is used in the extrusion of thick-walled titanium alloy profiles. It is formed into glass pads and placed between the billet and the die, providing essential lubrication to the die opening. This reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass lubricants for hot extrusion processes
TLC-1150-15
Blue-white particle
Horizontal extrusion
1150 ~ 1180℃
Application: Glass lubricant for hot extrusion is used in the extrusion of nickel-based alloys. It is formed into glass pads and placed between the billet and the die, providing essential lubrication to the die opening. This reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the nickel-based alloy extrusion process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass lubricant for stainless steel hot piercing process
TLC-GCK-7
Fine-white powder
Hot piercing
1100 ~ 1220℃
Application: Glass lubricant for the hot piercing process in stainless steel applications is applied to the piercing mandrel. It protects the mandrel and lubricates the inner wall of the tube during the hot piercing process. This reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the stainless steel hot piercing operation.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Coating powder with glass lubricant for hot piercing process
TLC-GCK-10-9
Yellow-white podwer
Hot piercing
1100 ~ 1220℃
Application: Glass lubricant for the hot piercing process is applied as an external coating powder. It is used in the hot piercing process by rolling onto the billet's outer surface. This application protects the guide plate, eliminates spiral marks on the billet surface, reduces friction, and ensures smooth material flow, thereby enhancing the efficiency and quality of the hot piercing process.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for titanium alloy hot piercing process
TLC-TCK-10
White powder
Titanium hot perforation
950 ~ 1000℃
Application: Glass powder for titanium alloy hot piercing is used in the hot piercing process by coating the piercing mandrel. This application protects the mandrel and lubricates the inner wall of the tube, reducing friction and wear. It ensures smooth material flow, enhances the efficiency of the process, and improves the quality of the pierced titanium alloy tubes.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass powder for hot extrusion process of tantalum alloy
TLC-Ta-1350
White powder
Horizontal extrusion
1000 ~ 1350℃
Application: Glass powder for tantalum alloy hot extrusion is used as an external coating powder in the hot extrusion process. It is applied by sprinkling onto the billet surface. This application provides essential lubrication, reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the hot extrusion process for tantalum alloys.
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass lubricant for molybdenum alloy hot extrusion process
TLC-Mo60
White powder
Horizontal extrusion
1000 ~ 1350℃
Application: Glass lubricant for molybdenum alloy hot extrusion is used as an external coating powder in the hot extrusion process. It is applied by sprinkling onto the billet surface. This application provides essential lubrication, reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the hot extrusion process for molybdenum alloys
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
Glass lubricant for tungsten alloy hot extrusion process
TLC-W33
White powder
Horizontal extrusion
1000 ~ 1350℃
Application: Glass lubricant for tungsten alloy hot extrusion is used as an external coating powder in the hot extrusion process. It is applied by sprinkling onto the billet surface. This application provides crucial lubrication, reduces friction and wear, ensures smooth material flow, and significantly enhances the efficiency and quality of the hot extrusion process for tungsten alloys
Product name:
P/N number:
Appearance:
Applicable Process:
Operation temperature:
High temperature grease for hot extrusion process
TLC-XBY-16
Black liquid
High temperature grease
300 ~ 400℃ coating
Application: High-temperature grease for hot extrusion processes is applied to lubricate extrusion punches and the inner walls of extrusion cylinders. This application reduces friction and wear, ensures smooth material flow, and enhances the efficiency and quality of the hot extrusion process. It is essential for maintaining equipment longevity and improving the performance of the extrusion process.